Phaetus Hardened Steel Nozzle
USD$9.60Add to wishlist Add to compare
In 3D printing filaments, composite consumables containing abrasive additives such as carbon fiber, steel, wood, boron carbide, tungsten and phosphorescent pigments are often very hard.The use of ordinary nozzle printing, will soon wear holes and inner diameter, destroying the original performance of the nozzle.
And Mohs type hardness of the hardened steel nozzle is 7.8, the highest printing temperature is 450℃, with high wear resistance, high temperature resistance. The hardened steel nozzle is the user’s first choice for printing high strength filaments!
DLC coating on whole nozzle surface with its hardness HV2500, thickness 2μm, and friction coefficient 0.03; Fine finish, low adhesion, high wear resistance.
Superior quality imported high-speed steel bars, special post-treatment, high temperature hardness up to HRC62.
Overall high temperature resistance 450℃, suitable for PEEK and other special engineering plastics printing.
Min. hole diameter 0.2mm (±0.01mm) to meet special application requirements and enable high accuracy printing.
Special processing technology and post-treatment ensure fine orifice and high smooth inner hole.
Wear-resistance, high temperature performance, suitable for 3D printing composites with abrasive additives such as Carbon Fiber, Steel, Wood, Boron Carbide, Tungsten and Phosphorescent pigment as well as conventional materials.
Min. Orifice Diameter
Inner Hole Roughness
PS (RepRap M6), PMK8 (MK8)
Φ0.10, Φ0.15, Φ0.20, Φ0.25, Φ0.30, Φ0.35, Φ0.40, Φ0.50, Φ0.60, Φ0.80, Φ1.00